Structural and magnetic properties of molecular beam epitaxy (MnSb2Te4)x(Sb2Te3)1-x topological materials with exceedingly high Curie temperature

Abstract: Tuning magnetic properties of magnetic topological materials is of interest to realize elusive physical phenomena such as quantum anomalous hall effect (QAHE) at higher temperatures and design topological spintronic devices. However, current topological materials exhibit Curie temperature (TC) values far below room temperature. In recent years, significant progress has been made to control and optimize TC, particularly through defect engineering of these structures. Most recently we showed evidence of TC values up to 80K for (MnSb2Te4)x(Sb2Te3)1-x, where x is greater than or equal to 0.7 and less than or equal to 0.85, by controlling the compositions and Mn content in these structures. Here we show further enhancement of the TC, as high as 100K, by maintaining high Mn content and reducing the growth rate from 0.9 nm/min to 0.5 nm/min. Derivative curves reveal the presence of two TC components contributing to the overall value and propose TC1 and TC2 have distinct origins: excess Mn in SLs and Mn in Sb2-yMnyTe3QLs alloys, respectively. In pursuit of elucidating the mechanisms promoting higher Curie temperature values in this system, we show evidence of structural disorder where Mn is occupying not only Sb sites but also Te sites, providing evidence of significant excess Mn and a new crystal structure:(Mn1+ySb2-yTe4)x(Sb2-yMnyTe3)1-x. Our work shows progress in understanding how to control magnetic defects to enhance desired magnetic properties and the mechanism promoting these high TC in magnetic topological materials such as (Mn1+ySb2-yTe4)x(Sb2-yMnyTe3)1-x.