Impact of capping agent on structural and optical properties of ZnS nanoparticles (2304.13420v1)

Abstract: Nanocrystalline samples of pristine capped and uncapped zinc sulphide were synthesized via the sol-gel technique. The nanocrystallinity of the samples were confirmed by the X-ray diffraction technique, where size of the particle size decreases with the increasing of mol. concentration (x = 0.00, 0.02, 0.03, 0.04 Mol). of capping agent sodium dodecyle sulphate. The obtained crystallite sizes were found to be in the range 4.6 nm to 2.7 nm respectively. The optical band gaps of the samples were estimated by using ultra-violet visible spectroscopic techniques and the band gap values were in the range 3.8 eV to 4.4 eV. All the samples showed quantum confinement behavior compared to bulk sample. Fluorescence (FL) spectra showed three emission peaks at the emission wavelengths around 434 nm, 520 nm, 545 nm, 628 nm, and 694 nm. The FL intensities were proportional to the concentration of capping agent.