Pressure-induced double-dome superconductivity in doped kagome metal Cs(V0.86Ta0.14)3Sb5 without charge density wave

Abstract: The vanadium-based kagome superconductor CsV$<em>3$Sb$_5$ exhibits an intricate interplay between charge density wave (CDW) and superconductivity (SC). Substituting Ta for V will suppress the CDW order and enhance superconductivity. Here, we report a high-pressure study up to 48 GPa on Ta-doped Cs(V$</em>{0.86}$Ta$<em>{0.14}$)$_3$Sb$_5$ with enhanced $T</em>\mathrm{c}$ around 5.29 K and without CDW order. At low pressures, unlike the characteristic $``$M-shaped" temperature-pressure phase diagram of the pristine CsV$<em>3$Sb$_5$, the Ta-doped compound exhibits a distinct non-monotonic evolution. Initially, $T</em>\mathrm{c}$ drops slightly from 5.29 K at ambient pressure to 4.90 K at 0.33 GPa, before increasing to a maximum of 5.70 K at 0.61 GPa. Upon further compression, $T_\mathrm{c}$ decreases continuously to 0.98 K at 12.3 GPa. At higher pressures, $T_\mathrm{c}$ rises again, reaching 4.46 K at 47.7 GPa. This evolution of $T_\mathrm{c}$ establishes two superconducting domes under pressure, which are similar to those in CsV$_3$Sb$_5$. Our results demonstrate that pressure-induced double-dome superconductivity is intrinsic to these V-based kagome superconductors, even in the absence of long-range CDW order.