The influence of Zn$^{2+}$ ions on the local structure and thermochromic properties of Cu$_{1-x}$Zn$_x$MoO$_4$ solid solutions

Abstract: The influence of zinc ions on the thermochromic properties of polycrystalline Cu${1-x}$Zn$_x$MoO$_4$ ($x$=0.10, 0.50, 0.90) solid solutions was studied by X-ray absorption spectroscopy at the Cu, Zn and Mo K-edges. Detailed structural information on the local environment of metal ions was obtained from the simultaneous analysis of EXAFS spectra measured at three metal absorption edges using the reverse Monte Carlo method. Thermochromic phase transition with the hysteretic behaviour between $\alpha$ and $\gamma$ phases was observed in Cu${0.90}$Zn$_{0.10}$MoO$_4$ solid solution. It was found that the local environment of molybdenum ions is most susceptible to the substitution of copper for zinc and, upon cooling, transforms from tetrahedral MoO$_4$ to distorted octahedral MoO$_6$.