Engineering Dzyaloshinskii-Moriya interaction in B20 thin film chiral magnets (1802.05107v1)

Abstract: Chiral magnetic Mn$x$Fe${1-x}$Ge compounds have an antisymmetric exchange interaction that is tunable with the manganese stoichiometric fraction, $x$. Although millimeter-scale, polycrystalline bulk samples of this family of compounds have been produced, thin-film versions of these materials will be necessary for devices. In this study, we demonstrate the growth of epitaxial Mn$x$Fe${1-x}$Ge thin films on Si (111) substrates with a pure B20 crystal structure in the stoichiometric fraction range x from 0 to 0.81. Following systematic physical and magnetic characterization including microwave absorption spectroscopy, we quantify the antisymmetric exchange interaction and helical period as a function of $x$, which ranges from 200 nm to 8 nm. Our results demonstrate an approach to engineering the size of magnetic skyrmions in epitaxial films that are grown using scalable techniques.