Probing the core and shell contributions to exchange bias in Co/Co$_3$O$_4$ nanoparticles of controlled size

Abstract: Coupling at the interface of core/shell magnetic nanoparticles is known to be responsible for the exchange bias (EB) and the relative sizes of core and shell components are supposed to influence the associated phenomenology. In this work, we have prepared core/shell structured nanoparticles with the total averaged diameter around $\sim$ 27 nm and a wide range of shell thicknesses through the controlled oxidation of Co nanoparticles well dispersed in an amorphous silica host. Structural characterizations give compelling evidence of the formation of Co$_3$O$_4$ crystallite phase at the shells surrounding the Co core. Field cooled hysteresis loops display nonmonotonous dependence of the exchange bias $H_E$ and coercive $H_C$ fields, that become maximum for a sample with an intermediate shell thickness, at which lattice strain is also maximum for both the phases. Results of our atomistic Monte Carlo simulations of the particles with the same size and compositions as in experiments are in agreement with the experimental observations and have allowed us to identify a change in the contribution of the interfacial surface spins to the magnetization reversal giving rise to the maximum in $H_E$ and $H_C$.