Fully dry PMMA transfer of graphene on h-BN using a heating/cooling system (1511.07117v1)

Abstract: The key to achieve high-quality van der Waals heterostructure devices made of stacking various two-dimensional (2D) layered materials lies in the clean interface without bubbles and wrinkles. Although polymethylmethacrylate (PMMA) is generally used as a sacrificial transfer film due to its strong adhesion property, it is always dissolved in the solvent after the transfer, resulting in the unavoidable PMMA residue on the top surface. This makes it difficult to locate clean interface areas. In this work, we present a fully dry PMMA transfer of graphene onto h-BN using a heating/cooling system which allows identification of clean interface area for high quality graphene/h-BN heterostructure fabrication. The mechanism lies in the utilization of the large difference in thermal expansion coefficients between polymers (PMMA/PDMS) and inorganic materials (graphene/h-BN substrate) to mechanically peel off PMMA from graphene by the thermal shrinkage of polymers, leaving no PMMA residue on the graphene surface. This method can be applied to all types of 2D layered materials.