High Seebeck coefficient and ultra-low lattice thermal conductivity in Cs2InAgCl6 (1802.08136v1)

Abstract: The elastic, electronic and thermoelectric properties of indium-based double-perovskite halide, Cs2InAgCl6 have been studied by first principles study. The Cs2InAgCl6 is found to be elastically stable, ductile, anisotropic and relatively low hard material. The calculated direct bandgap 3.67 eV by TB-mBJ functional fairly agrees with the experimentally measured value 3.3 eV but PBE functional underestimates the bandgap by 1.483 eV. The relaxation time and lattice thermal conductivity have been calculated by using relaxation time approximation (RTA) within the supercell approach. The lattice thermal conductivity (\k{appa}l) is quite low (0.2 Wm-1K-1). The quite low phonon group velocity in the large weighted phase space, and high anharmonicity (large phonon scattering) are responsible for small \k{appa}l. The room temperature Seebeck coefficient is 199 {\mu}VK-1. Such high Seebeck coefficient arises from the combination of the flat conduction band and large bandgap. We obtain power factors at 300K by using PBE and TB-mBJ potentials are ~29 and ~31 mWm-1K-2, respectively and the corresponding thermoelectric figure of merit of Cs2BiAgCl6 are 0.71 and 0.72. However, the maximum ZT value obtained at 700K is ~0.74 by TB-mBJ potential. The obtained results implies that Cs2InAgCl6 is a promising material for thermoelectric device applications.