Cracking predictions of lithium-ion battery electrodes by X-ray computed tomography and modelling (2202.09572v1)

Abstract: Fracture of lithium-ion battery electrodes is found to contribute to capacity fade and reduce the lifespan of a battery. Traditional fracture models for batteries are restricted to consideration of a single, idealised particle; here, advanced X-ray computed tomography (CT) imaging, an electro-chemo-mechanical model and a phase field fracture framework are combined to predict the void-driven fracture in the electrode particles of a realistic battery electrode microstructure. The electrode is shown to exhibit a highly heterogeneous electrochemical and fracture response that depends on the particle size and distance from the separator/current collector. The model enables prediction of increased cracking due to enlarged cycling voltage windows, cracking susceptibility as a function of electrode thickness, and damage sensitivity to discharge rate. This framework provides a platform that facilitates a deeper understanding of electrode fracture and enables the design of next-generation electrodes with higher capacities and improved degradation characteristics.