Reversible Photo-Induced Phase Segregation and Origin of Long Carrier Lifetime in Mixed-Halide Perovskite Films (2110.05246v1)

Abstract: Mixed-halide based hybrid perovskite semiconductors have attracted tremendous attention as a promising candidate for high efficient photovoltaic and light-emitting devices. However, these advanced perovskite materials may undergo phase segregation under light illumination due to halide ion migration, affecting their optoelectronic properties. Here, we report photo-excitation induced phase segregation in triple-cation mixed-halide perovskite films that yields to red-shift in photoluminescence response. We demonstrate that photo-excitation induced halide ion migration leads to the formation of smaller-bandgap iodide-rich and larger-bandgap bromide-rich domains in the perovskite film, where the phase segregation rate is found to follow the excitation power-density as a power law. Results confirm that charge carrier lifetime increases with redshift in photoluminescence due to the trapping of photo-excited carriers in the segregated smaller-bandgap iodide-rich domains. Interestingly, we found that these photo-induced changes are fully reversible and thermally activated when the excitation power is turned off. A significant difference in activation energies for halide ion migration is observed during phase segregation and recovery process under darkness. Additionally, we have investigated the emission linewidth broadening as a function of temperature which is governed by the exciton-optical phonon coupling. The mechanism of photo-induced phase segregation is interpreted based on excitonphonon coupling strength in both mixed and demixed (segregated) states of perovskite film.